Effects of workpiece preheating on surface roughness, chatter and tool performance during end milling of hardened steel D2

Amin, A. K. M. Nurul and Dolah, Shuriani and Mahmud, Marlina and Lajis, M. A. (2008) Effects of workpiece preheating on surface roughness, chatter and tool performance during end milling of hardened steel D2. Journal of Materials Processing Technology, 201 (1-3). pp. 466-470. ISSN 0924-0136

[img] PDF (Effect of workpiece preheating on surface roughness, chatter, and tool life on end milling of hardened steel ) - Published Version
Restricted to Registered users only

Download (1MB) | Request a copy

Abstract

This paper presents the results of experimental investigations conducted on a vertical machining centre (VMC) to ascertain the effectiveness of brazed circular polycrystalline cubic boron nitride (PCBN) inserts in end milling of hardened steel AISI D2 (60–62 HRC), under room temperature and workpiece preheated conditions. Comparison was made in terms of intensity of chatter, chip formation instability, tool wear and metal removal capacity of the tool and surface roughness of the machine parts. It has been found that chips formed are composed of primary and secondary serrated teeth and their formative frequencies have definite relationship with the chatter frequencies. Though initial average flank wear of the tool during preheated machining is found to be slightly higher compared to that of room temperature machining, the extrapolated tool life appears to be higher in the case of preheating. The main mechanisms of tool failure are found to be superficial plastic deformation, diffusion and notching. It has been observed that feed per tooth, cutting speed, preheating and amplitude of chatter have direct bearing on the surface roughness. It has been observed that preheated machining of the material leads to surface roughness values well below 0.4_m, such that the operations of grinding as well as polishing can be avoided at the higher cutting speeds.

Item Type: Article (Journal)
Additional Information: 2872/17338
Uncontrolled Keywords: Hardened steel AISI D2, Poly crystalline cubic boron nitride (PCBN), Chatter, Tool wear, and surface finish
Subjects: T Technology > TJ Mechanical engineering and machinery
T Technology > TS Manufactures
Kulliyyahs/Centres/Divisions/Institutes (Can select more than one option. Press CONTROL button): Kulliyyah of Engineering > Department of Manufacturing and Materials Engineering
Depositing User: Dr. A.K.M. Nurul Amin
Date Deposited: 10 Apr 2012 14:57
Last Modified: 10 Apr 2012 14:57
URI: http://irep.iium.edu.my/id/eprint/17338

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year