Effect of voltage on the consolidation of tic particulates on steel substrate fused by TIG welding arc

Mridha, Shahjahan and Md. Idriss, A. N. and Maleque, Md. Abdul and -, Suryanto and Mohamad, Souad A. (2011) Effect of voltage on the consolidation of tic particulates on steel substrate fused by TIG welding arc. In: Regional Tribology Conference 2011, 22-24 November 2011, Langkawi, Malaysia.

PDF ( Effect of voltage on the consolidation of tic particulates on steel substrate fused by TIG welding arc) - Published Version Restricted to Repository staff only Download (776kB) | Request a copy

Abstract

Surface alloying with ceramic powder uses a high energy input to create composite coating that provides protection against wear and corrosion. In this work TiC incorporated composite coating was created by melting single tracks in 1.0 mg/mm2 TiC powder preplaced on alloy steel surfaces using a conventional TIG welding torch produced at 80 ampere current with a voltage between 30 to 55V and a constant traversing speed of 1.0 mm/s. The effect of voltage, used to generate TIG torch for melting, was investigated in terms of geometry, microstructure and hardness of the processed track. The TIG torch produced with different voltages created melt pool of hemispherical shape with varying track dimensions. The melt dimensions increased with increasing voltage. Glazing with 30 V created a melt pool of 3.10mm wide and 0.80 mm deep; the maximum width of 3.96mm and depth of 0.97 mm was produced at 55 V and 45 V, respectively. Tracks produced under different conditions were free from cracks but pores were seen in places. The melt microstructures consisted of partially dissolved and unmelted TiC particulates along with dendrites of a variety of TiC precipitates. Agglomeration of TiC was apparent at the edges. The population of TiC precipitates and partially dissolved TiC particulates increased when glazed at high voltage torch. Hardness development was lowest when glazed at 30 V and it increased by glazing at 35 and 45 V. The population of TiC particulates and their sizes were seen to influence the hardness and this phenomenon is also similar for the precipitated particlesHardness development was lowest when glazed at 30 V and it increased by glazing at 35 and 45 V. The population of TiC particulates and their sizes were seen to influence the hardness and this phenomenon is also similar for the precipitated particles.

Item Type:	Conference or Workshop Item (Full Paper)
Additional Information:	3925/7341
Uncontrolled Keywords:	Tungsten inert gas (TIG) torch, Voltage, Low alloy steel, Composite layer, Agglomeration of TiC, Hardness
Subjects:	T Technology > TN Mining engineering. Metallurgy T Technology > TS Manufactures
Kulliyyahs/Centres/Divisions/Institutes (Can select more than one option. Press CONTROL button):	Kulliyyah of Engineering > Department of Manufacturing and Materials Engineering
Depositing User:	Prof Dr. Md Abdul Maleque
Date Deposited:	02 Dec 2011 11:52
Last Modified:	02 Dec 2011 15:07
URI:	http://irep.iium.edu.my/id/eprint/7341

Actions (login required)

View Item