The tribological behaviour of Fe-C-Al cast iron – effect of temperature

Maleque, Md. Abdul and Sugrib , S. (2013) The tribological behaviour of Fe-C-Al cast iron – effect of temperature. Industrial Lubrication and Tribology, 65 (5). pp. 320-327. ISSN 0036-8792

[img] PDF (The tribological behaviour of Fe-C-Al cast iron – effect of temperature) - Published Version
Restricted to Repository staff only

Download (595kB) | Request a copy

Abstract

Purpose - The aim of this paper is to study the tribological behaviour of Fe-C-Al cast iron at different temperatures using universal pin-on-disk machine. Design/methodology/approach - The cold set resin bonded sand mould casting process was employed to develop Fe-C-Al cast iron and Fe-C-Si cast iron. The microstructures of materials were studied using field emission scanning electron microscope. The wear and friction tests were conducted using universal pin-on-disk machine at 25 0C, 100 0C, 200 0C and 300 0C temperature. The wear damage surface was characterized using scanning electron microscopy. Findings - The lower wear rate was found for Fe-C-Al cast iron compared to Fe-C-Si cast iron and delamination type wear morphology was observed in both types of cast iron materials. The results also showed that the friction coeficient value of Fe-C-Al cast iron was lower than Fe-C-Si cast iron at different temperature. It can be concluded that the overall tribological behaviour of Fe-C-Al cast iron at higher temperature was better than conventional Fe-C-Si cast iron. Originality/value - The information on the development and tribological properties of the Fe-C-Al cast iron at different temperatures is scare in literature. The special type of cold set resin bonded sand mould was used for casting this Fe-C-Al cast iron material. Therefore, current study is quite new and it is hoped that it will provide a high value to the automotive and other engineering researchers for the application of this material.

Item Type: Article (Journal)
Additional Information: 6103/26904
Uncontrolled Keywords: Temperature, Wear, Cast iron, Surface analysis, Profilometry.
Subjects: T Technology > TN Mining engineering. Metallurgy > TN600 Metallurgy
Kulliyyahs/Centres/Divisions/Institutes (Can select more than one option. Press CONTROL button): Kulliyyah of Engineering > Department of Manufacturing and Materials Engineering
Depositing User: Prof Dr. Md Abdul Maleque
Date Deposited: 24 Jul 2013 11:04
Last Modified: 22 Aug 2013 08:47
URI: http://irep.iium.edu.my/id/eprint/26904

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year