Synthesis, characterisation and stability of superparamagnetic maghemite nanoparticle suspension

Nurdin, Irwan and Johan, Mohd Rafie and Yaacob, Iskandar Idris and Ang, Beechin and Andriyana, Andri (2014) Synthesis, characterisation and stability of superparamagnetic maghemite nanoparticle suspension. Materials Research Innovations, 18. S6-200-S6-203-S6-203. ISSN 1432-8917 E-ISSN 1433-075X

[img] PDF - Published Version
Restricted to Repository staff only

Download (215kB) | Request a copy
[img] PDF (Scopus) - Supplemental Material
Restricted to Repository staff only

Download (486kB) | Request a copy

Abstract

Maghemite nanoparticles were synthesised using the co-precipitation method and characterised by various techniques, including X-ray diffraction, transmission electron microscopy, alternating gradient magnetometry, dynamic light scattering and zeta potential. The stability of the suspension was monitored by measuring the particle size distribution and zeta potential using dynamic light scattering over a period of few months. The pattern obtained from X-ray diffraction confirmed that the particles were maghemite with crystallite size of 94 nm. Transmission electron microscopy observations and analyses showed that the mean physical size of the nanoparticles was 95 nm. The nanoparticles show superparamagnetic behaviour with magnetisation value at ±10 kOe of 3218 emu g-1. The intensity averaged particle size of as-synthesised maghemite nanoparticles was 453 nm. The suspension was stored for periods of 2, 4 and 8 months. The intensity averaged sizes were 471, 505 and 521 nm respectively. No sedimentation was observed. The suspension's zeta potential value was 446 mV for as-synthesised sample and 433, 427 and 418 mV for sample after storage period of 2, 4 and 8 months, respectively. This indicated that the suspension was very stable.

Item Type: Article (Journal)
Additional Information: 6524/58539
Uncontrolled Keywords: Maghemite; Magnetic materials; Nanoparticle; Stability Superparamagnetic
Subjects: Q Science > QE Geology
T Technology > TA Engineering (General). Civil engineering (General)
Kulliyyahs/Centres/Divisions/Institutes (Can select more than one option. Press CONTROL button): Kulliyyah of Engineering
Kulliyyah of Engineering > Department of Mechanical Engineering
Depositing User: Prof. Dr. Iskandar Idris Yaacob
Date Deposited: 26 Sep 2017 14:08
Last Modified: 26 Sep 2017 14:08
URI: http://irep.iium.edu.my/id/eprint/58539

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year