Preparation of zinc doped-biphasic calcium phosphate/carbon nanotube composites

-, Gunawan and Sopyan, Iis and Mel, Maizirwan and -, Suryanto (2014) Preparation of zinc doped-biphasic calcium phosphate/carbon nanotube composites. Advances in Environmental Biology, 8 (3(Spe)). pp. 787-791. ISSN 1995-0756 E-ISSN 1998-1066

	PDF - Published Version Restricted to Registered users only Download (396kB) | Request a copy
	PDF (SCOPUS) - Supplemental Material Restricted to Repository staff only Download (72kB) | Request a copy

Abstract

Biphasic calcium phosphate (BCP) has been used in tissue engineering and orthopedics due to its good biocompatibility and osteoconductivity. However, its clinical applications are usually limited by the low strength and brittleness. The objective of this research was to develop Zn-doped BCP composites in which multi-wall carbon nanotubes (MWCNT) were introduced to the Zn-doped BCP ceramic matrix to improve the mechanical properties of the resulting composites. The starting powders have been synthesized via sol-gel method. Zinc concentration was varied in the range of 0, 1, 2, 4, 5, and 10mol%. After uniaxial pressing the compacted samples were sintered via conventional pressureless sintering. The samples were studied in terms of the phase stability, relative density, Vickers hardness, and fracture toughness as well as in vitro analysis in SBF solution. The results showed that hydroxyapatite as the main phase and β-tricalcium phosphate as the secondary phase of obtained powders. The morphology of the powders show the formation of nanocrystalline powder and individual particles are globular in shape.The maximum micro Vickers hardness and fracture toughness was achieved when fired at 1200oC, with 4.30 GPa and 2.0 MPa.m1/2, respectively. In vitro analysis shows that the samples have been covered by apatite cell since day one, and the density of apatite increased with immersion time in SBF. This study showed that CNT reinforcing was beneficial in producing high toughness of BCP without offsetting its bioactivity properties.

Item Type:	Article (Journal)
Additional Information:	4809/37559
Uncontrolled Keywords:	Biomaterials, Composite, Characterization, Zinc doping, Biphasic calcium phosphate, Carbone nanotubes, Mechanical, Simulated body fluid.
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA164 Bioengineering
Kulliyyahs/Centres/Divisions/Institutes (Can select more than one option. Press CONTROL button):	Kulliyyah of Engineering > Department of Biotechnology Engineering Kulliyyah of Engineering > Department of Manufacturing and Materials Engineering Kulliyyah of Engineering > Department of Mechanical Engineering
Depositing User:	PROF. DR. IIS SOPYAN
Date Deposited:	04 Aug 2014 14:50
Last Modified:	18 Aug 2017 16:04
URI:	http://irep.iium.edu.my/id/eprint/37559

Actions (login required)

View Item