Analysis on tool wear during milling carbon fiber reinforced polymer in dry, coolant and chilled air condition

Mustafa, Aisyah Madihah and Abd Halim, Nor Farah Huda and Tomadi, Siti Haryani and Shahruddin, Najlah Sakinah and Nasaruddin, Ricca Rahman (2023) Analysis on tool wear during milling carbon fiber reinforced polymer in dry, coolant and chilled air condition. Jurnal Tribologi, 36 (March 2023). pp. 99-107. E-ISSN 2289-7232

[img] PDF - Published Version
Restricted to Registered users only

Download (895kB) | Request a copy
[img] PDF - Published Version
Restricted to Repository staff only

Download (258kB) | Request a copy

Abstract

The demand of the Carbon Fiber Reinforced Polymer (CFRP) has been significantly increasing over the years especially in automotive and aerospace since CFRP possesses an excellent strength-to-weight ratio. However, milling CFRP challenging due to its anisotropic and heterogeneous property therefore produce brittle and dust-like chips. As CFRP is a combination of layers of carbon fibers embedded in matrix resin, machining process must be conducted below the glass transition temperature (Tg) of the matrix resin as it can degrade the CFRP. In this experimentto investigate the effect of cutting speed and cutting conditions on the tool wear during the milling process, CFRP was machined with 6mm diameter uncoated tungsten carbide tool with helix angle of 30°. Milling of CFRP was performed with three cutting speeds of 130, 150 and 170 m/min in three different cutting conditions which is dry, coolant and chilled air with constant feed rate of 2100 mm/min and depth of cut of 2 mm. The highest average tool wear of 110 μm was obtained during milling the CFRP with cutting speed 170 m/min in chilled air condition, 25.5% higher than the average wear of 82 μm at low cutting speed of 130 m/min in the same condition.

Item Type: Article (Journal)
Subjects: T Technology > T Technology (General)
T Technology > T Technology (General) > T175 Industrial research. Research and development
T Technology > TJ Mechanical engineering and machinery
Kulliyyahs/Centres/Divisions/Institutes (Can select more than one option. Press CONTROL button): Kulliyyah of Engineering
Kulliyyah of Engineering > Department of Biotechnology Engineering
Kulliyyah of Engineering > Department of Manufacturing and Materials Engineering
Depositing User: Dr Nor Farah Huda Abd Halim
Date Deposited: 06 Apr 2023 08:41
Last Modified: 08 Jun 2024 10:16
URI: http://irep.iium.edu.my/id/eprint/104281

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year