IIUM Repository

Morphology of electrospun PVA nanofibers enhanced with graphene oxide, Poly (3,4 ethylenedioxythiophene):polystyrene sulfonate (PEDOT:PSS), and multiwalled carbon nanotubes

Ahmad Shahizam, Zayd and Benoudjit, Abdel Mohsen and Mohamad, Nurnazihah and Abd-Wahab, Firdaus and Wan Salim, Wan Wardatul Amani (2020) Morphology of electrospun PVA nanofibers enhanced with graphene oxide, Poly (3,4 ethylenedioxythiophene):polystyrene sulfonate (PEDOT:PSS), and multiwalled carbon nanotubes. Experimental and Theoretical Nanotechnology, 4 (3). pp. 235-248. E-ISSN 2590-4132

[img] PDF (In-press article) - Submitted Version
Restricted to Repository staff only

Download (2MB) | Request a copy
[img] PDF (Acceptance letter) - Supplemental Material
Restricted to Repository staff only

Download (161kB) | Request a copy
Official URL: http://etn.siats.co.uk/

Abstract

Morphology of poly(vinyl alcohol) (PVA) nanofibers was studied while varying needle-collector distance and concentrations of graphene oxide, poly (3,4-ethylenedioxythiophene):polystyrene sulfonate (PEDOT:PSS), and functionalized multiwalled carbon nanotubes. Most notably, we found that variations in PVA nanofiber diameter of ~ 34 nm exist in the radial area of electrospinning; the variation is believed to be the result of a fringing electric field effect at the edge of the collector plates. Needle-collector distance was varied between 10 and 17 cm, and FESEM images revealed average fiber diameter decreased from 173 nm to 144 nm with no obvious change in morphology at both nanofiber diameters. Similarly, electrospinning of PVA-GO solution at 17 cm resulted in nanofibers with decreased average diameter of 197 nm (σ = 97 nm), compared with PVA alone (349 nm, σ = 87 nm) with no obvious change in morphology. The average diameter of PVA nanofibers then increased with added PEDOT:PSS to 244 nm, σ = 75 nm. PVA-MWCNT samples at 2 wt% and 4 wt% showed no beading, while at 6, 8, and 10 wt%, beads were prevalent in the fibers. The presence of beads could be the result of re-agglomeration of MWCNTs in the electrospinning solution at higher wt%. No clear trend was found with increasing concentrations of MWCNTs, with average nanofiber diameters varying in the range of 115 – 206 nm.

Item Type: Article (Journal)
Additional Information: 5236/78513
Uncontrolled Keywords: Electrospinning; nanofiber morphology; PVA; graphene oxide; PEDOT:PSS; MWCNTs
Subjects: R Medicine > R Medicine (General)
T Technology > TP Chemical technology > TP248.13 Biotechnology
Kulliyyahs/Centres/Divisions/Institutes (Can select more than one option. Press CONTROL button): Kulliyyah of Engineering
Kulliyyah of Engineering > Department of Biotechnology Engineering
Depositing User: Dr Wan Wardatul Amani Wan Salim
Date Deposited: 04 Mar 2020 11:38
Last Modified: 19 Jan 2021 15:21
URI: http://irep.iium.edu.my/id/eprint/78513

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year