Incorporation of TIC particulates on AISI 4340 low alloy steel surfaces via tungsten inert gas arc melting

Mridha, Shahjahan and Idriss, A.N. Md and Baker, Neville Incorporation of TIC particulates on AISI 4340 low alloy steel surfaces via tungsten inert gas arc melting. Advanced Materials Research. ISSN 1022-6680 (Unpublished)

[img] PDF (Incorporation of TIC particulates on AISI 4340 low alloy steel surfaces via tungsten inert gas arc melting) - Accepted Version
Restricted to Repository staff only

Download (585kB) | Request a copy

Abstract

Surface cladding utilizes a high energy input to deposit a layer on substrate surfaces providing protection against wear and corrosion. In this work, TiC particulates were incorporated by melting single tracks in powder preplaced onto AISI 4340 low alloy steel surfaces using a Tungsten Inert Gas (TIG) torch with a range of processing conditions. The effects of energy input and powder content on the melt geometry, microstructure and hardness were investigated. The highest energy input (1680J/mm) under the TIG torch produced deeper (1.0 mm) and wider melt pools, associated with increased dilution, compared to that processed at the lowest energy (1008J/mm). The melt microstructure contained partially melted TiC particulates associated with dendritic, cubic and globular type carbides precipitated upon solidification of TiC dissolved in the melt; TiC accumulated more near to the melt-matrix interface and at the track edges. Addition of 0.4, 0.5 and 1.0 mg/mm2 TiC gave hardness values in the resolidified melt pools between 750 to over 1100Hv, against a base hardness of 300 Hv; hardness values are higher in tracks processed with a greater TiC addition and reduced energy input.

Item Type: Article (Journal)
Additional Information: 3925/6139
Uncontrolled Keywords: Low alloy steel, TIG torch, TiC powder, Surface layer, Microstructure, Melt depth, Hardness
Subjects: T Technology > TN Mining engineering. Metallurgy > TN600 Metallurgy
Kulliyyahs/Centres/Divisions/Institutes: Kulliyyah of Engineering > Department of Manufacturing and Materials Engineering
Depositing User: Prof. Dr. Shahjahan Mridha
Date Deposited: 06 Dec 2011 14:31
Last Modified: 06 Dec 2011 14:47
URI: http://irep.iium.edu.my/id/eprint/6139

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year