Effect of carburization process on adhesion strength of ti carbide layer on titanium alloy substrate

Sudin, Izman and Abdul-Kadir, Mohammed Rafiq and Anwar, Mahmood and Engku Abu Bakar, Engku Mohd Nazim and Nalisa, Adila and Konneh, Mohamed (2011) Effect of carburization process on adhesion strength of ti carbide layer on titanium alloy substrate. Advanced Materials Research, 197. pp. 219-224. ISSN 1022-6680

PDF (Effect of Carburization Process) - Published Version Restricted to Repository staff only Download (6MB) | Request a copy

Abstract

Titanium alloys are commonly used in biomedical application in hard tissues replacement especially for knee and hip implants. Surface modifications are required prior to diamond coating process for improving tribological and wear properties of the titanium alloy. In this study, experiments were carried out to investigate the effects of different carburizing times on the adhesion strength of carbide layer formed on the Ti-6Al-7Nb. Prior to carburization process, all samples were treated to remove residual stress and oxide scales by annealing and pickling processes respectively. Hard wood charcoal powder was used as a medium. The carburizing process was carried out for 6, 12 and 24 hours at 950 °C under normal atmospheric condition. Surface morphology, carbide layer thickness and adhesion strength were evaluated using SEM, XRD, 3D Surface Profilometer and Blast Wear Tester (BWT). It is found that a mixture of oxide and carbide layers formed on the substrate and the thickness of these layers increases with carburizing time. It is also revealed that the 24 hr carburizing time provides the strongest adhesion strength among the three and TiC as the dominant layer.

Item Type:	Article (Journal)
Additional Information:	4486/3171
Uncontrolled Keywords:	Biomedical, Ti-6Al-7Nb, Sustainability, Carburization, Titanium Alloy
Subjects:	T Technology > TJ Mechanical engineering and machinery
Kulliyyahs/Centres/Divisions/Institutes (Can select more than one option. Press CONTROL button):	Kulliyyah of Engineering > Department of Manufacturing and Materials Engineering
Depositing User:	Dr Mohamed Konneh
Date Deposited:	27 Sep 2011 15:51
Last Modified:	29 Dec 2011 12:09
URI:	http://irep.iium.edu.my/id/eprint/3171

Actions (login required)

View Item