Initial response in antibacterial activity of orthopaedic metal implant coated with silver composite

Mohd Jan, Nurul Hafiza and Zulkifly, Ahmad Hafiz and Ibrahim, Mohd Zulfadzli and Sha'ban, Munirah (2017) Initial response in antibacterial activity of orthopaedic metal implant coated with silver composite. In: Fundamental Science Congress 2017 (FSC2017), 21st-22nd Nov. 2017, Serdang, Selangor. (Unpublished)

[img] PDF - Published Version
Restricted to Repository staff only

Download (18MB) | Request a copy

Abstract

Introduction: The objective of this study was to investigate the potential effect of silver coated orthopaedic metal implant against biofilm-producing staphylococcus aureus through an in vitro experimental setting. Our hypothesis was that orthopaedic implant coated with silver would exert both bacteriostatic and bactericidal effects against staphylococcus aureus. Materials & methods: The silver coated plate was soaked with 200ml of phosphate buffered saline (PBS) in shaking water bath at 37˚C for silver release preparation. 5.0ml solution was collected at 1-, 3-, 24-, 48-, 168-, 336- and 504-hour time point for analyses. Bacterial inoculation was smeared on sterile nutrient agar media. Plain discs placement were loaded on the surface of nutrient agar. 20µl silver release solution in each assessment was loaded on the plain disc. 20µl of PBS also was loaded on the plain disc and used as control. All samples were incubated at 37 ˚C for 24 hours for bacterial culture under aerobic condition. The samples were incubated up to 168 hours under the same conditions for assessment. The antibacterial effect was evaluated based on the diameter of inhibition zone using disc diffusion test. Results and Discussions: Bacterial colony was noted on the surface of nutrient agar after 24 hours incubation. However, the inhibition zone with a diameter more than 20mm was noted at 168 hours of silver release after 168 hours incubation. The outcome of this study revealed positive indicator of the silver as antibacterial agent. Conclusion: This result suggested that orthopaedic metal implant coated with silver composite may provide antibacterial protection against medical device-related infection.

Item Type: Conference or Workshop Item (Speech/Talk)
Additional Information: 2397/60163
Uncontrolled Keywords: Silver Coated, Orthopaedic Implant, Silver Release, Antibacterial Activity.
Subjects: Q Science > QR Microbiology
R Medicine > RD Surgery > RD701 Orthopedics
Kulliyyahs/Centres/Divisions/Institutes (Can select more than one option. Press CONTROL button): Kulliyyah of Medicine > Department of Department of Orthopaedics, Traumatology & Rehabilitation
Kulliyyah of Allied Health Sciences > Department of Physical Rehabilitation Sciences
Depositing User: Mr. Mohd Zulfadzli Ibrahim
Date Deposited: 15 Dec 2017 10:46
Last Modified: 15 Dec 2017 10:46
URI: http://irep.iium.edu.my/id/eprint/60163

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year