Sol-gel derived zinc doped calcium phosphate bioceramics prepared via different sintering strategies

Sopyan, Iis and Gunawan, - and -, Suryanto (2014) Sol-gel derived zinc doped calcium phosphate bioceramics prepared via different sintering strategies. In: International Conference on Advances in Manufacturing and Materials Engineering (ICAMME2014), 23rd-25th September 2014, Kuala Lumpur. (Unpublished)

[img] PDF
Restricted to Repository staff only

Download (625kB) | Request a copy
[img] PDF
Restricted to Repository staff only

Download (1MB) | Request a copy

Abstract

Sinterability of zinc doped calcium phosphate (CaP) sintered via conventional pressureless and two step sintering methods was investigated. The starting powders have been synthesized through sol-gel method with zinc concentration varied in the range of 0, 1, 4, and 10mol%. After uniaxial pressing, the compacts were sintered via conventional pressureless sintering. The dense samples were studied in terms of the phase stability, relative density, Vickers hardness, and fracture toughness. The phase of samples was hydroxyapatite and β-tricalcium phosphate. The presence of Zn caused a change in the sintering behaviour of dense calcium phosphate. Zn doping has improved relative density of 4mol% Zn-doped by 8.1% compared to undoped fired at 1300oC. The maximum fracture toughness of 1.43 MPa.m1/2 and Vickers hardness of 3.44 GPa were achieved at 1200oC by 4 mol% Zn-doped. The low Vickers hardness and fracture toughness obtained for dense samples sintered of two step sintering compared to conventional pressureless sintering is due to the low measured bulk density. This study showed that conventional pressureless sintering was beneficial in producing high toughness of Zn doped CaP.

Item Type: Conference or Workshop Item (UNSPECIFIED)
Additional Information: 4805/41465
Uncontrolled Keywords: sintering, conventional, two step, method, zinc doping, calcium phosphate, bioceramics, characterization
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA164 Bioengineering
Kulliyyahs/Centres/Divisions/Institutes (Can select more than one option. Press CONTROL button): Kulliyyah of Engineering
Depositing User: Dr - Suryanto
Date Deposited: 16 Feb 2015 10:40
Last Modified: 18 Jun 2018 23:19
URI: http://irep.iium.edu.my/id/eprint/41465

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year