The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k

Ani, Mohd Hanafi and Othman, Raihan (2012) The effects of water vapor on high temperature oxidation of Fe-Cr-Ni alloy at 1073k. Research Report. s.n., Kuala Lumpur. (Unpublished)

[img] PDF - Submitted Version
Restricted to Registered users only

Download (817kB) | Request a copy

Abstract

Void formation in oxide scale during high temperature oxidation is a common phenomenon. Over a long period of time voids will affect the mechanical property of scales by influencing the cracking and spalling. Voids formed in dry environment are different than that of formed in humid environment. With the presence of water vapor in humid environment the formation of void will increase, thus greater number of void compared to that in dry environment

Item Type: Monograph (Research Report)
Additional Information: 4583/32502
Uncontrolled Keywords: high temperature oxidation, Fe-Cr-Ni alloy, void formation, quantitative analysis of void, dry environment, humid environment
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
T Technology > TK Electrical engineering. Electronics Nuclear engineering
Kulliyyahs/Centres/Divisions/Institutes: Kulliyyah of Engineering > Department of Manufacturing and Materials Engineering
Depositing User: Sr. Norsyaziela Zulkefli
Date Deposited: 18 May 2015 10:01
Last Modified: 18 May 2015 10:01
URI: http://irep.iium.edu.my/id/eprint/32502

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year