Sintering of hydroxyapatite ceramic produced by wet chemical method

Singh, Ramesh and Ranna, Tolouei and Tan, Chou Yong and K. L., Aw and W., H. Yeo and Iis, Sopyan and Teng, Wan Dung (2011) Sintering of hydroxyapatite ceramic produced by wet chemical method. Advanced Materials Research, 264/65. pp. 1856-1861. ISSN 1022-6680

[img] PDF (Sintering of Hydroxyapatite Ceramic Produced by Wet Chemical Method) - Published Version
Restricted to Repository staff only

Download (203kB) | Request a copy

Abstract

In the present work, densification of synthesised hydroxyapatite (HA) bioceramic prepared via chemical precipitation method was investigated. HA samples was prepared by compaction at 200 MPa and sintered at temperatures ranging from 800°C to 1400°C. The results revealed that the HA phase was stable for up to sintering temperature of 1250°C. However, decomposition of HA was observed in samples sintered at 1300°C with the formation of tetra-calcium phosphate (TTCP) and CaO. Samples sintered above 1400°C were found to melt into glassy phases. The bulk density increases with increasing temperature and attained a maximum value of 3.14 gcm-3 at 1150°C whereas maximum hardness value of 6.64 GPa was measured in HA sintered at 1050°C. These results are discussed in terms of the role of grain size. © (2011) Trans Tech Publications, Switzerland.

Item Type: Article (Journal)
Additional Information: 4089/21423
Uncontrolled Keywords: Hydroxyapatite, Bioceramic, Sintering
Subjects: T Technology > TS Manufactures
Kulliyyahs/Centres/Divisions/Institutes (Can select more than one option. Press CONTROL button): Kulliyyah of Engineering
Kulliyyah of Engineering > Department of Manufacturing and Materials Engineering
Depositing User: PROF. DR. IIS SOPYAN
Date Deposited: 24 Feb 2012 11:14
Last Modified: 24 Feb 2012 11:14
URI: http://irep.iium.edu.my/id/eprint/21423

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year