Formation of Ti-Al-N dispersed composite layer on steel by TIG torch surface cladding

Sarker, Dyuti and Mridha, Shahjahan and Shaha, Sugrib Kumar (2010) Formation of Ti-Al-N dispersed composite layer on steel by TIG torch surface cladding. In: International Conference on Materials Processing Technology 2010, 5 - 6 January, 2010, Bangkok, Thailand.

[img] PDF (Formation of Ti-Al-N dispersed composite layer on steel by TIG Torch surface cladding)
Restricted to Registered users only

Download (353kB) | Request a copy

Abstract

In this study an attempt has been made to produce titanium-aluminium dispersed hard nitride layer on mild steel surfaces by preplacement of 50% Ti and 50% Al powder mixture and then melting with TIG torch under nitrogen environment. Parameter such as heat input of the torch was varied between 540, 608 and 675 J/mm and its effect on the resolidified melt pool was studied. Glazing under all energy inputs produced more than 1mm thick resolidified clad layer. The microstructural analysis revealed the clad layer with dispersion of dendrites of Ti-Al nitrides and Ti-Al intermetallic in ferrite matrix. The concentration of dendrites were found to be maximum near the surface and decreased at deeper depths.The maximum hardness of the modified surface layer was found to be 900 Hv compared to180 Hv of the mild steel substrate.

Item Type: Conference or Workshop Item (Full Paper)
Additional Information: 3925/1677
Uncontrolled Keywords: Composite layer, dendrite, intermetallic, hardness
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Kulliyyahs/Centres/Divisions/Institutes: Kulliyyah of Engineering
Kulliyyah of Engineering > Department of Manufacturing and Materials Engineering
Depositing User: Ms Zati Atiqah Mohamad Tanuri
Date Deposited: 25 Aug 2011 11:14
Last Modified: 07 Sep 2011 08:27
URI: http://irep.iium.edu.my/id/eprint/1677

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year